Fiberglass Surface Tissue (FRP surface Tissue)
Fiberglass surface tissue is characterized as uniform fiber dispersion, smooth surface and fast resin impregnation. It is mainly used as the surface layer of FRP products， whose capability is ameliorated. It is capable of significantly improving the strength of FRP surface layer, with strong impaction resistance, excellent uniformity of surface, good covering up the texture of under layers and good corrosion resistance.
1) Hand lay-up type FRP surface tissue
Hand lay-up type FRP surface tissue is mainly applied in the production of hand lay-up FRP products. It has the advantages of good pattern fitness and quick resin permeating. It is also characterized as covering up the texture of layers, making the surface smooth and improving FRP product’s service life.
|
Items |
Unit |
Hand lay-up type FRP surface tissue |
||||
|
F-BM(H)20 |
F-BM(H)30 |
F-BM(H)40 |
F-BM(H)50 |
F-BM(H)-60 |
||
|
Fiber Diameter |
μ m |
9 /13 |
||||
|
Area weight |
g/m 2 |
20 |
30 |
40 |
50 |
60 |
|
Binder Content |
% |
5-8 |
||||
|
Penetrating time (two layers) |
S |
8 |
10 |
15 |
20 |
25 |
|
Tensile Strength MD |
N/ 50mm |
35 |
40 |
50 |
60 |
70 |
|
Moisture content |
% |
0.2 |
||||
|
Roll Width |
mm |
The roll width can be produced according to the customers' requirement. |
2) Wrap type FRP surface tissue
Wrap type FRP surface tissue is mainly applied in wrapping FRP pipes and vessels. It has absorbed a great deal of resin and the defendable layer formed on the FRP product surface. It is capable of significantly improving the performances of surface layer to strengthen longer lifetime and resistance against corrosion, leakage and compression．
<table width="100%" border="0" cellspacing="0" cellpadding="0" class="table"
|
Items |
Unit |
Wrap type FRP surface tissue |
||||
|
F-BM(W)20 |
F-BM(W)30 |
F-BM(W)40 |
F-BM(W)50 |
F-BM(W)60 |
||
|
Monofilament Diameter |
μ m |
9-12 |
||||
|
Area weight |
g/m 2 |
20 |
30 |
40 |
50 |
60 |
|
Binder Content |
% |
6-9 |
||||
|
Penetrating time(two layers) |
S |
8 |
10 |
15 |
20 |
25 |
|
Tensile Strength MD |
N/50mm |
35 |
40 |
50 |
60 |
70 |
|
Moisture content |
% |
0.2 |
||||
|
Roll Width |
mm |
The roll width can be produced according to the customers' requirement. |
3) Pull trussing type surface tissue
Pull trussing type surface tissue could improve the strength of profiled material surface layer. It can ameliorate the capability and avoid crack of the product.
<table width="100%" border="0" cellspacing="0" cellpadding="0" class="table"
|
Items |
Unit |
Type |
||
|
F-BM(P)-90 |
F-BM(P)-105 |
F-BM(P)-120 |
||
|
Monofilament Dia. |
μ m |
9 / 12 |
||
|
Area weight |
g/m 2 |
90 |
105 |
120 |
|
Binder Content |
% |
25 |
||
|
Penetrating time(two layers) |
S |
25 |
30 |
40 |
|
Tensile Strength MD |
N/ 50mm |
280 |
300 |
350 |
|
Tensile Strength CD |
N/ 50mm |
180 |
200 |
230 |
|
Moisture content |
% |
0.2 |
||
|
Roll Width |
mm |
The roll width can be produced according to the customers' requirement.. |